Polyamide 6 and 66 Compounds Reinforced with Glass Fibers

Product Introduction:

PA66 polyamide compound with fibers exhibits very good resistance, physical and mechanical properties. However, one of the weak points of this material is that it hydrolyzes when placed in the vicinity of water. Hydrolysis causes the loss of material properties over time. The mentioned compound has the ability to service at high temperature, and has high resistance to hydrolysis and high strength.

The presence of polyamide in the vicinity of water and heat causes its hydrolysis, and the hydrolysis of the material causes the destruction of the material, loss of properties and defects in the performance of the final piece. The product developed by the company is a compound of polyamide resistant to hydrolysis and impact.

Technical Specifications:

* Density: 0.03±1.35

* Ash Content: 2±30 %

* Tensile Strength At Break: ≥155 Mpa

* Elongation At Break: ≥%2

* Notched Izod Impact: 20 Kj/m2

* High tensile strength, %30 increase in breaking strength for this component compared to ordinary polyamide 66 and 6, from 83 MPa to 10 MPa

* Thermal resistance at high temperatures with a thermal deformation temperature of 234.5˚C

Advantages:

* High volume of production

* Customization